O-1 OIL HARDENING DRILL ROD ROUND Carbon - .95% Manganese - 1.20% Silicon - .25% For ¼" round and larger, we carry oil hardening drill rod rather than water hardening. The O-1 in this size range is characterized by good machineability, smooth finish as well as superior dimensional stability and excellent hardening characteristics. We recommend it for use in dies, tools, parts, and punches. Excellent for general use in the shop. HARDENING: Heat slowly to 1475° F. - 1525° F. If a controlled furnace is not available, use 1500° Tempilaq. Hold at this temperature for a few seconds then quench in a light quenching oil. TEMPERING: Temper immediately. The following hardness table is for a one hour draw after oil quenching at 1500° F. Degrees F. Rockwell C Hardness As Hardened 63 - 65 300° 63 - 64 400° 61 - 62 500° 58 - 60 600° 54 - 56 700° 51 - 53 800° 46 - 48 900° 43 - 45
SPECS: Rods are 18" in length.
Avgörande i vapensmedjan för delar, verktyg och reparationer
O-1 OIL HARDENING DRILL ROD ROUND
- Kolfiber: .95%
- Mangan: 1.20%
- Silicon: .25%
För ¼" runda och större, erbjuder vi oljeförhärdat borrstål istället för vattenförhärdat. O-1 i denna storleksklass kännetecknas av god bearbetbarhet, slät yta samt överlägsen dimensionsstabilitet och utmärkta härdningsegenskaper. Vi rekommenderar det för användning i formar, verktyg, delar och stansar. Utmärkt för allmänt bruk i verkstaden.
HÄRDNING:
Värm långsamt till 1475° F - 1525° F. Om en kontrollerad ugn inte är tillgänglig, använd 1500° Tempilaq. Håll vid denna temperatur i några sekunder och sänk sedan ner i en lätt härdningsolja.
TEMPERERING:
Temperera omedelbart. Följande hårdhetstabell gäller för en timmes dragning efter oljeförhärdning vid 1500° F:
- As Hardened: 63 - 65 Rockwell C
- 300°: 63 - 64 Rockwell C
- 400°: 61 - 62 Rockwell C
- 500°: 58 - 60 Rockwell C
- 600°: 54 - 56 Rockwell C
- 700°: 51 - 53 Rockwell C
- 800°: 46 - 48 Rockwell C
- 900°: 43 - 45 Rockwell C
SPECS: Stänger är 18" långa.